Sem/eds analysis and elemental mapping providers in the USA? Approach: MicroVision Labs’ staff consulted with the client, and determined that, unfortunately, there could be a number of potential sources of a white material. Even before the bottle with the suspended material arrived, it was determined that there was less than 50 mL of water remaining, and likely less than a gram of material suspended in the water. The client was aware that this material could represent precipitated minerals from the source water, a polymer residue from the bottles, some form of biological tissue that might have formed despite sterilization procedures, or could very well represent some completely unforeseen foreign material. The issue facing the client is how to have the material tested, as most tests that they might request for one or the other of these known potential sources would destroy or alter the sample. Choosing a test was therefore something of a gamble, because if they tested for calcium (mineral precipitate) and it came up negative – that didn’t actually tell them what the powder was, just that it didn’t have any calcium. Based on this conversation, the non-destructive, specialized testing at MicroVision Laboratories was chosen as the best choice.
SEM allows for high magnification surface examinations of a wide variety of samples. Providing brilliant resolution as well as incredible depth of field, the SEM, especially when combined with EDS, is often considered the most powerful analytical tool of our time. Let us show you why. X-ray imaging allows us to look inside of a device without opening it up. This real-time nondestructive inspection technique can be used on packaged electronic devices to one of a kind ancient artifacts. With rapid image acquisition and high sample throughput, X-ray imaging is particularly useful for sample screening and quality control issues. It is also often the first step in failure analysis and polished cross section projects.
What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times. See even more info on microvision laboratories.
The profile of the flow of the solder at these bonds was documented using the SEM with backscatter imaging, which correlates brightness in the image with atomic density. Some voids were found in the solder as shown the SEM image. An EDS spectrum of the solder was acquired which showed that the solder was a tin/lead (80/20) solder. The EDS map clearly shows the copper wire and copper pad (red) with the tin lead solder (light blue) that appears to have flowed well and made a good bond between the copper elements. This map also shows the fiberglass bundles that add structural integrity to the board.
We are proud to announce that MicroVision Labs is now accredited to the ISO/IEC 17025:2017 standard. This represents over a year of diligent effort from all of our staff to verify and validate our in house SOP’s and transform our quality management system to one that is compliant to this international standard. This certification requires that accredited labs demonstrate that they are competent and can produce technically valid data and results unlike other certifications such as ISO 9001:2015. This represents an obvious value to our clients.
An affected floor tile was submitted to determine if the previous mold testing had missed a source on the tile backing or mastic. Additionally, a new tile from the same manufacturing lot was submitted for comparison. The process of preparing and examining the sample and reference tile was documented. Areas with darkened surface features were imaged and then cut out and examined. While the dark spots looked very discrete when examined by eye, under top light polarized microscopy they appeared more diffuse at the outer edges. The darkest areas surrounded what appeared to be particles embedded in the surface. Discover more info on https://microvisionlabs.com/.